Study on the lithium solid electrolytes of Li3N-Li3Bi-LiCl ternarysystem - 2Li(3)Bi center dot 3LiCl lithium solid electrolyte

ISL OpenIR > 青海盐湖研究所知识仓储

	Study on the lithium solid electrolytes of Li3N-Li3Bi-LiCl ternarysystem - 2Li(3)Bi center dot 3LiCl lithium solid electrolyte
	Yang, JX; Jia, YZ; Yao, ZX
	1997
发表期刊	SOLID STATE IONICS
ISSN	0167-2738
卷号	96 期号:3-4 页码:215-218
摘要	Lithium solid electrolyte 2Li(3)Bi . SLiCl was prepared and was characterized by X-ray diffraction and X-ray photoelectron spectroscopy (XPS). The electrical conductivity of the prepared sample was determined from room temperature to 250 degrees C by PAR 368-1 AC-impedance spectrometer. The frequency measurement range was between 4 Hz and 100 kHz. The experimental results showed that the 2Li(3)Bi . 3LiCl lithium solid electrolyte has a high conductivity of about 1 x 10(-4) S/cm at 100 degrees C and 1 x 10(-2) S/cm at 350 degrees C. Lithium solid electrolyte 2Li(3)Bi . SLiCl was prepared and was characterized by X-ray diffraction and X-ray photoelectron spectroscopy (XPS). The electrical conductivity of the prepared sample was determined from room temperature to 250 degrees C by PAR 368-1 AC-impedance spectrometer. The frequency measurement range was between 4 Hz and 100 kHz. The experimental results showed that the 2Li(3)Bi . 3LiCl lithium solid electrolyte has a high conductivity of about 1 x 10(-4) S/cm at 100 degrees C and 1 x 10(-2) S/cm at 350 degrees C.
文献类型	期刊论文
条目标识符	http://ir.isl.ac.cn/handle/363002/2386
专题	青海盐湖研究所知识仓储中国科学院青海盐湖研究所
推荐引用方式 GB/T 7714	Yang, JX,Jia, YZ,Yao, ZX. Study on the lithium solid electrolytes of Li3N-Li3Bi-LiCl ternarysystem - 2Li(3)Bi center dot 3LiCl lithium solid electrolyte[J]. SOLID STATE IONICS,1997,96(3-4):215-218.
APA	Yang, JX,Jia, YZ,&Yao, ZX.(1997).Study on the lithium solid electrolytes of Li3N-Li3Bi-LiCl ternarysystem - 2Li(3)Bi center dot 3LiCl lithium solid electrolyte.SOLID STATE IONICS,96(3-4),215-218.
MLA	Yang, JX,et al."Study on the lithium solid electrolytes of Li3N-Li3Bi-LiCl ternarysystem - 2Li(3)Bi center dot 3LiCl lithium solid electrolyte".SOLID STATE IONICS 96.3-4(1997):215-218.